| Color | Solid Tone Colors |
| Viscosity | 16-16.3 sec. #2 Zahn |
| Percent of Solids (%) | 46 |
| V.O.C | Exempt per CFR 51.1 / Regulation 8 |
| RoHS | Compliant |
| REACH | Compliant |
| Halogens | None |
| Thermal Stability. Resin (cured) | 1200°F + / 648.8°C + |
|
Conical Bond (1/4” Mandrel) (ASTM D522-93a) |
Passed |
| Cross Cut Adhesion (ASTM D3359) | 5B |
| Coefficient of Friction (ASTM D2047) | 0.05µ |
| Specific Gravity (ASTM D891-09) | 0.9 |
| Pencil Hardness (ASTM D3363) | 9h + |
| Salt Fog Test (ASTM B117) | 3500 hours |
| Odor (liquid) | Slight Solvent |
| Odor (cured) | None |
- Overview
- Technical Data
- Key Performance Properties
- Drying and Coverage Rate
- Supplemental Information
- Common Applications
- Resources
AT 1420 – ALPHASHIELD ELITE (MILITARY GRADE)
AT 1420 - AlphaShield Elite is the ultimate firearm coatings developed specifically for military small arms and crew-served weapon applications. AT 1420 effectively manages the visual and near-infrared signature while at the same time enhancing thermal protection and durability. It offers superior wear and corrosion resistance in extreme conditions. AT 1420 maintains peak performance under conditions where competing products fail.
The coating is tough, durable and provides long term protection against corrosion, weathering, and abrasion. Unlike most competing products, AT 1420 also offers high temperature insulation performance. AT 1420 is only available for sale to military and law enforcement agencies.
Proudly manufactured in the USA.
- High performance single component coating.
- Extreme adhesion. Forms covalent bond to the substrate giving it an intrinsic bond to surfaces
- Very tough and durable.
- Excellent UV, chemical and abrasion resistance.
- High anti-corrosion performance.
- Extreme heat & flame resistance (1200°F+/648°C+)
- Unparalleled thermal insulation protection
- Conform to NIR reflectivity standards outlined in MIL-DTL-44436
- Easy to apply. Curable by ambient air (accelerated oven curing possible)
- May be applied to metal and non-metal surfaces
- VOC exempt
- RoHS and REACH compliant
| Average Applied Dry Film Thickness |
2 to 5 microns (0.4 – 1 mil) |
| Estimated Coverage Rate (@ 3 microns) | 6,250 ft² (580 m²) per gallon |
|
Dry to Touch Time (@ 77°F / 25°C) *Exposing to a warmer air flow (not exceeding 110°F) will decrease dry time |
15 – 25 minutes (average) |
| Ambient Cure (Full Properties) | 5 days |
|
Cure Time (@350°F) *Oven cure only after coating is dry to touch |
30 – 40 minutes (average) |
Also available:
- AT 1405 – AlphaShield Grip*
- AT 1410 – AlphaShield Ultra for maximum performance
- AT 1420 – AlphaShield Elite (military grade)
- AT 1450 – AlphaShield Bore Coat (dry lubricant)
*Textured feel can also be added if desired.
**Available in a wide variety of colors.
Any firearm component that requires high temperature protection including suppressor, barrel, muzzle brake, rail and handgrip.