| Color | Clear |
| Viscosity | 16-18 sec. #2 Zahn |
| Percent of Solids (%) | 18 |
| V.O.C | Exempt per CFR 51.1 / Regulation 8 |
| RoHS | Compliant |
| REACH | Compliant |
| Halogens | None |
| Thermal Stability (cured) | 1200°F (648.8°C) |
|
Conical Bond (1/8” Mandrel) (ASTM D522-93a) |
Passed |
|
Cross Cut Adhesion (ASTM D3359) |
5B |
|
Coefficient of Friction (ASTM D2047) |
0.03µ |
|
Specific Gravity (ASTM D891-09) |
0.889 |
|
Pencil Hardness (ASTM D3363) |
8-9h |
| Odor (liquid) | Slight Solvent |
| Odor (cured) | None |
- Overview
- Technical Data
- Key Performance Properties
- Drying and Coverage Rate
- Supplemental Information
- Common Applications
- Resources
AT 1670 - ALPHATEK NON-STICK INDUSTRIAL BLADE BASE
AT 1670 is a high performance, single component coating specifically designed to protect and revitalize industrial blades. It creates a thin, incredibly durable ceramic protective layer on cutting surfaces. It revitalizes cutting surfaces by smoothing out imperfections caused by past corrosion pitting, uneven abrasion wear and general wear & tear. This creates a sharper, more efficient cutting surface. Secondly, the ceramic surface coating will protect the blade from future damage. The overall result is a sharper, more efficient cutting tool that performs better, lasts longer and requires less maintenance. AT 1670 is easily applied by wipe in ambient conditions.
Proudly manufactured in the USA
- Smoothens rough blade surfaces & reduces friction for maximum cutting performance
- Protects cutting edges from erosion and corrosion, thereby reducing maintenance and downtime
- Increase usable life of cutting equipment
- Creates a covalent bond to the substrate giving it an intrinsic bond to the cutting blade for maximum long term durability
- Contains no “free silicones” to contaminate finished products
- Clear finish
- Thin application
- Excellent coverage rate
- Easily applied by wiping
- Ambient cure, short dry time
- Environmentally friendly. VOC exempt.
- RoHS and REACH compliant
| Average Applied Dry Film Thickness | 2 to 3 microns |
|
Estimated Coverage Rate (@ 3 microns) |
2,450 ft² (60 m²/Liter) per gallon |
|
Dry to Touch Time (@ 77°F / 25°C) *Exposure to a warmer air flow (not exceeding 110°F) will accelerate drying times. |
15 – 25 minutes (average) |
AT 1671 can be used as a topcoat to create a “super slick” finish that will further improve cutting performance and longevity.
- Any type of industrial cutting blade, slitter, knife, razor, shear, etc.