| Color | Clear |
| Viscosity | 12 sec. #2 Zahn |
| Percent of Solids (%) | 12 |
| V.O.C | Exempt per CFR 51.1 / Regulation 8 |
| RoHS | Compliant |
| REACH | Compliant |
| Halogens | None |
| Thermal Stability (cured) | 1200°F (648.8°C) |
|
Conical Bond (1/8” Mandrel) (ASTM D522-93a) |
Passed |
|
Cross Cut Adhesion (ASTM D3359) |
5B |
|
Coefficient of Friction (ASTM D2047) |
0.03µ |
|
Specific Gravity (ASTM D891-09) |
0.889 |
|
Pencil Hardness (ASTM D3363) |
8h |
| Odor (liquid) | Slight Solvent |
| Odor (cured) | None |
- Overview
- Technical Data
- Key Performance Properties
- Drying and Coverage Rate
- Supplemental Information
- Common Applications
- Resources
AT 2600 - ALPHATEK MOLD RELEASE
AT 2600 - AlphaTek Mold Release coating revolutionizes composites manufacturing. It maximize ROI via a simple to apply coating that improves both the efficiency and longevity of molds. It results in faster cycle times due to easier release. AT 2600 drives more cycles without cleaning or re-coating. No free silicones means no contamination of molded components. AT 2600 works with all common high temperature resin systems and all common industrial-molding technologies.
Proudly manufactured in the USA.
- High performance single component mold release film.
- Easy application. May be wiped on and ambient air cured.
- Creates a covalent bond to the substrate giving it an intrinsic bond to the mold.
- Inert (benign) material.
- Excellent release properties with all common high temperature cured resin systems (e.g. epoxy, BMI, polyurethane, and polyimide).
- Very low transfer (contamination) to the molded part. No free silicones.
- Excels at releasing difficult substrates from complex mold geometries.
- High suitability for no rubber-to-metal bonding.
- Low levels of in-mold build-up/fouling.
- Many releases (high durability) between applications.
- Applicable to all common molding processes.
- High temperature resistance.
- Available with black light tracer to ensure 100% coverage.
- RoHS and REACH compliant.
| Average Applied Dry Film Thickness | 2 to 3 microns |
|
Estimated Coverage Rate (@ 3 microns) |
1,630 ft² (150 m²) per gallon |
|
Dry to Touch Time (@ 77°F / 25°C) *Exposure to a warmer air flow (not exceeding 110°F) will accelerate drying and curing |
15 – 25 minutes (average) |
AT 2600(BL) is available with black light tracer for easily inspecting coating coverage once applied.
All common molding and composite manufacturing processes