| Color | Colorless Liquid |
|
Viscosity (ASTM D1084B) |
1.0 cps @ 74°F (23°C) |
| Percent of Solids (%) | <38 |
| V.O.C | Exempt per CFR 51.1 / Regulation 8 |
| RoHS | Compliant |
| REACH | Compliant |
| Halogens | None |
| Thermal Stability. Resin (cured) | 1200°F + (648.8°C +) |
|
Conical Bond (1/8” Mandrel) (ASTM D522-93a) |
Passed |
|
Cross Cut Adhesion (ASTM D3359) |
5B |
|
Specific Gravity (ASTM D891-09) |
0.810 |
| Odor (liquid) | Slight Solvent |
| Odor (cured) | None |
- Overview
- Technical Data
- Key Performance Properties
- Drying and Coverage Rate
- Supplemental Information
- Common Applications
- Resources
AT 510 - ALPHATEK PRIMER
AT 510 - AlphaTek Primer is a VOC exempt, solvent based, hybrid-ceramic clear primer that provides adhesion in a wide variety of demanding environments. It adheres to almost anything and almost anything will adhere to it. AT 510 can be used as a primer on almost any substrate or as an intra-coating adhesive. AT 510 is tough, durable and adheres to almost any surface. This coating is suitable for operating temperatures of up to 148°F (64.8°C).
Proudly manufactured in the USA.
- Excellent adhesion to almost any surface.
- Creates an intrinsic covalent bond with most substrates.
- Compatible with most topcoats.
- Remains flexible.
- Smooth, clear finish.
- High operating temperature.
- Effective for both hot and cold applications.
- Thin application.
- Excellent coverage rate.
- Easily applied by wipe or spray.
- Ambient cure, short dry time.
- Environmentally friendly. VOC exempt.
- RoHS and REACH compliant.
| Average Applied Dry Film Thickness | 1 to 3 micron |
|
Estimated Coverage Rate (@3 microns) |
5,200 ft² (480 m²) per gallon |
| Dry Time (@ 65-70°F / 18-21°C) | 5 – 10 minutes |
- For higher temperature applications, use AT 520.
- AT 510 is compatible with AlphaTek’s complete line of Nano-Ceramic Clear and Color Coatings as well as most commercial coatings found in the market. Contact your AlphaTek representative for more information.
- As a primer to provide adhesion for a topcoat, particularly when the substrate cannot be cleaned of all contaminants prior to coating (e.g. waxes or silicones) or the desired topcoat lacks adhesion.
- Intra-coating adhesive to allow the build of multiple layers of other coating products.